TL-15 water-based anti-rust/anti-corrosion coating :
|
Specifications |
|
|
Characteristics |
1. Excellent adhesion and hardness.
2. Excellent performance against oil/water/organic solvent/humidity. 3. No volatilizable organic compounds. Diluted and cleaned by water, no poisons and no waste of chemicals. 4. Bear to 800℃ up momentary temperature and 400℃ up, incombustible and nonflammable. 5. Fast drying,can be recoated or touched in 2 hours. can be used in places of poor-ventilation,no danger of explosion or poison.。
|
|
Physical characteristics |
|
|
color |
gray |
|
specific gravity |
1.26g/cm3 (20℃) |
|
ＶＯＣ |
none |
|
ＴＶＯＣ |
none |
|
Capability against brushing/cleaning |
More than 2000 times |
|
Capability against alkali |
More than 3000 hours |
|
Water resistance |
More than 3000 hours |
|
package |
20 kg/PE bucket、200 kg/PE bucket |
|
thinner |
Pure water |
|
Application details |
|
|
Preparation before use |
Steel surface should be treated by sand blast to s.a 2.5 on the GB8923-88 rules |
|
Time for complete drying |
2 hours |
|
Application |
anti-rust/anti-corrosion for steel |
|
Application way |
Brushed/roller coating/air-spray spurting(best way is air-spray spurting) |
|
Diluting % |
Pure water(1~5%) |
|
Applying amount |
30㎡/Gal，8㎡/L，2.8㎡/kg ； 22㎡/Gal，6㎡/L，2㎡/kg |
|
Thickness of membrane |
3 mil (75μm) ； 4 mil (100μm) |
|
* Above mentioned are standard application details.Actual consuming amount may differ depending on steel-surface condition. |
|
|
Drying temperature |
25℃ |
|
Drying time(finger touch) |
≦20 minutes |
|
Drying time(firm solid) |
≦2 hours |
|
Applying interval |
≦2 hours |
|
Remarks |
1. ratios for zinc-powder and resin must be correct. 2. Must keep stirring while adding zinc-powder into resin,it's important and can't be mistaken.。 3. Can't be mixed with other coatings/thinners/organic solvents. 4. Can't be mixed with acids/alkali etc. 5. While taking a break,soak the spray-gun into water. 6. After job finished,discharge the coating in pipes,and clean it(also the spray-gun)by water.。
|